Finally, any other material properties (such as thermal expansion coefficients) should be set to the special cases for an isotropic material.
Finally, any other material properties (such as thermal expansion coefficients) should be set to the special cases for an isotropic material.


=== Fibrous Materials ===
== Effective Time Implementation ==


A potential use for a transversely isotropic viscoelastic material is to model fiber-reinforced composites including wood (although transversely isotropic is not a great model for wood because it cannot represent low transverse shear modulus compared to radial and tangential transverse tensile moduli). If the axial direction is the fiber direction, one might expect that time dependence will be much weaker in the axial direction than in the transverse direction. This behavior could be approximated by setting <math>n</math> and <math>\ell</math> independent of time. Because an elastic material has <math>n=E_A+4K_T\nu_A^2</math> and <math>\ell = 2K_t\nu_A</math>, this approximation implies <math>E_A</math>,  <math>K_T</math>, and <math>\nu_A</math> are all independent of time. The final result is that only <math>G_T(t)</math> and <math>G_A(t)</math> are time dependent. This model is one approximation, but would have zero creep in the axial direction and therefore no use in modeling that response (unless experiments also show zero creep).
This material handles effect of temperature and solvent concentration on relaxation times by the same methods used for [[Viscoelastic Material#Effective Time Implementation|isotropic viscoelastic materials]].


A second option might be to let <math>K_T(t)</math> depend on time while <math>E_A</math> and <math>\nu_A</math> remain independent of time. This approach does not work and results in non-physical response to axial loading. The problem appears that it predicts that <math>n(t)</math> decreases in time. For isotropic materials, <math>n(t)</math> increases in time and it also likely increases for fibrous materials as well. In brief, to model viscoelastic properties of fibrous material that might include effects in the axial direction, the modeling will need to input all five time-dependent properties allowed by this material. Those properties should be based on experimental observations.
== Elastic Mechanical Properties ==


== Effective Time Implementation ==
This material handles effect of temperature and solvent concentration on elastic properties by the same methods used for [[Viscoelastic Material#Elastic Mechanical Properties|isotropic viscoelastic materials]].
 
This material handles variations in temperature and solvent concentration by the same methods used for [[Viscoelastic Material#Effective Time Implementation|isotropic viscoelastic materials]].


== Material Properties ==
== Material Properties ==
Line 99: Line 97:
| Tref || Reference temperature to shift relaxation times using the WLF equation. If <tt>Tref</tt>&lt;0, then no shifting is done and relaxation times will be independent of temperature. || K || -1
| Tref || Reference temperature to shift relaxation times using the WLF equation. If <tt>Tref</tt>&lt;0, then no shifting is done and relaxation times will be independent of temperature. || K || -1
|-
|-
| C1 || Coefficient in WLF equation used when <tt>Tref</tt>&ge;0 to shift relaxation times || none || 17.44
| C1 || Coefficient in WLF equation used when <tt>Tref</tt>&ge;0 to shift relaxation times. If the entered value is negative, the thermal shift switches to Arrhenious activation energy with ''&Delta;H<sub>a</sub> = -RC<sub>1</sub>'', || none || 17.44
|-
|-
| C2 || Coefficient in WLF equation used when <tt>Tref</tt>&ge;0 to shift relaxation times || none || 51.6
| C2 || Coefficient in WLF equation used when <tt>Tref</tt>&ge;0 to shift relaxation times (not used if ''C<sub>1</sub>'' is negative). || none || 51.6
|-
|-
| mref || Reference concentration to shift relaxation times using the WLF-style equation. If <tt>mref</tt>&lt;0, then no shifting is done and relaxation times will be independent of concentration. || K || -1
| mref || Reference concentration to shift relaxation times using the WLF-style equation. If <tt>mref</tt>&lt;0, then no shifting is done and relaxation times will be independent of concentration. || K || -1
Line 108: Line 106:
|-
|-
| Cm2 || Coefficient in WLF-style equation used when <tt>mref</tt>&ge;0 to shift relaxation times (must be positive) || none || 0.0625
| Cm2 || Coefficient in WLF-style equation used when <tt>mref</tt>&ge;0 to shift relaxation times (must be positive) || none || 0.0625
|-
| bTemp<br>bTValue || Enter <tt>(bTemp,bTValue)</tt> pairs for piecewise interpolation of vertical temperature [[Viscoelastic Material#Elastic Mechanical Properties|shift of elastic properties]]. Enter any number of pairs with <tt>bTemp</tt> values monotonically increasing || (degrees,none) || none
|-
| bConc<br>bCValue || Enter <tt>(bConc,bCValue)</tt> pairs for piecewise interpolation of vertical concentration (or moisture) [[Viscoelastic Material#Elastic Mechanical Properties|shift of elastic properties]]. Enter any number of pairs with <tt>bConc</tt> values monotonically increasing. Enter with actual concentration and not concentration potential. || none || none
|-
|-
| [[Transversely Isotropic Material#Material Properties|TI Properties]] || Enter thermal expansion, solvent expansion, and poroelasticity properties as usual for transversely isotropic materials. || varies || varies
| [[Transversely Isotropic Material#Material Properties|TI Properties]] || Enter thermal expansion, solvent expansion, and poroelasticity properties as usual for transversely isotropic materials. || varies || varies
Line 116: Line 118:
|}
|}


The material properties need to define the time dependence 5 properties. The process for each one is to enter the long-term value first (GT0, GA0, KT0, en0, ell0) and then to follow each one by ntaus (only needed in <tt>XML</tt> files) and by one Pk and tauk value for each term in the series. The elastic values for each property are calculated from the value at time = zero. Other elastic properties are then found from
The material properties need to define the time dependence 5 properties. The process for each one is to enter the long-term value first (GT0, GA0, KT0, en0, ell0) and then to follow each one by ntaus (only needed in <tt>XML</tt> files) and by one Pk and tauk value for each term in the series. Elastic value, or the property values at time zero, are sums of all Pk terms for that property. For example:
 
&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;
<math>G_T(0) = G_{T0} + \sum_{k=1}^{N_{GT}} G_{Tk}
</math>
 
Other elastic properties are given by
 
&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;
&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;
<math>\nu_A(0) = {\ell(0)\over 2K_T(0)}
<math>\nu_A(0) = {\ell(0)\over 2K_T(0)}
Line 122: Line 131:
E_A(0) = n(0) - 4K_T(0)\nu_A^2 = n(0) - \frac{\ell(0)^2}{K_T(0)}
E_A(0) = n(0) - 4K_T(0)\nu_A^2 = n(0) - \frac{\ell(0)^2}{K_T(0)}
</math>
</math>
&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;
&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;
<math>\frac{1}{E_T(0)} = \frac{1}{4K_T(0)} +\frac{1}{4G_T(0)} + {\nu_A(0)^2\over E_A(0)}
<math>\frac{1}{E_T(0)} = \frac{1}{4K_T(0)} +\frac{1}{4G_T(0)} + {\nu_A(0)^2\over E_A(0)}
\qquad {\rm and} \qquad
\qquad {\rm and} \qquad
\nu_T(0) = \frac{E_T(0)}{2G_T(0)}-1
\nu_T(0) = \frac{E_T(0)}{2G_T(0)}-1
</math>
The above initial values, or the properties at time zero, are sums of all Pk terms for that property. For example
&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;
<math>G_T(0) = G_{T0} + \sum_{k=1}^{N_{GT}} G_{Tk}
</math>
</math>



Latest revision as of 14:22, 1 May 2024

Constitutive Law

This anisotropic MPM material is a small strain, linear viscoelastic material that extends the Viscoelastic Material to model anisotropic viscoelasticity. The stress (σ) and strain (ε) are related by:

      [math]\displaystyle{ \sigma(t) = \mathbf{C}(t) * \varepsilon(t) }[/math]

Here [math]\displaystyle{ * }[/math] indicates convolution (or Boltzman's superposition) between time-dependent stiffness tensor ([math]\displaystyle{ \mathbf{C}(t) }[/math]) and strain tensor. In Voight-notation with unique axis in the z direction, the time-dependent stiffness tensor is

      [math]\displaystyle{ \mathbf{C}(t) = \left[\begin{array}{cccccc} K_T(t)+G_T(t) & K_T(t)-G_T(t) & \ell(t) & 0 & 0 & 0 \\ K_T(t)-G_T(t) & K_T(t)+G_T(t) & \ell(t) & 0 & 0 & 0 \\ \ell(t) & \ell(t) & n(t) & 0 & 0 & 0 \\ 0 & 0 & 0 & G_A(t) & 0 & 0 \\ 0 & 0 & 0 & 0 & G_A(t) & 0 \\ 0 & 0 & 0 & 0 & 0 & G_T(t) \end{array}\right] }[/math]

Here [math]\displaystyle{ K_T(t) }[/math] is the plane strain, bulk modulus, [math]\displaystyle{ G_T(t) }[/math] is the transverse shear modulus, [math]\displaystyle{ G_A(t) }[/math] is the axial shear modulus, and [math]\displaystyle{ n(t) }[/math] and [math]\displaystyle{ \ell(t) }[/math] give time-dependence of the C33 and C13=C23 elements of the stiffness tensor (as defined here). The time dependence of each property is modeled with a sum of exponentials:

      [math]\displaystyle{ K_T(t) = K_{T0} + \sum_{k=1}^{N_{KT}} K_{Tk} e^{-t/\tau_{KT,k}} \qquad G_T(t) = G_{T0} + \sum_{k=1}^{N_{GT}} G_{Tk} e^{-t/\tau_{GT,k}} \qquad G_A(t) = G_{A0} + \sum_{k=1}^{N_{GA}} G_{Ak} e^{-t/\tau_{GA,k}} }[/math]

      [math]\displaystyle{ n(t) = n_0 + \sum_{k=1}^{N_n} n_k e^{-t/\tau_{n,k}} \qquad\qquad \ell(t) = \ell_0 + \sum_{k=1}^{N_\ell} \ell_k e^{-t/\tau_{\ell,k}} }[/math]

In terms of axial modulus [math]\displaystyle{ E_A }[/math], and Poisson's ratio, [math]\displaystyle{ \nu_A }[/math], we can write:      

      [math]\displaystyle{ n(t) = E_A(t) + 4K_T(t)\nu_A(t)^2 \qquad\qquad \ell(t) = 4K_T(t)\nu_A(t) }[/math]

This material lumps all these time dependencies into [math]\displaystyle{ n(t) }[/math] and [math]\displaystyle{ \ell(t) }[/math], but note that selection of those properties will determine time dependencies of [math]\displaystyle{ E_A(t) }[/math] and [math]\displaystyle{ \nu_A(t) }[/math]

      [math]\displaystyle{ \nu_A(t) = {\ell(t)\over 2K_T(t)} \qquad {\rm and} \qquad E_A(t) = n(t) - \frac{\ell(t)^2}{K_T(t)} }[/math]

Rotated Material Axes

The initial axial direction is along the z axis (or θ axis for axisymmetric calculations). The axial direction can be changed to any other direction using the same method used to orient transversely isotropic elastic material with the swapz material property.

Isotropic with Time-Dependent Bulk Modulus

The available isotropic viscoelastic material is limited to materials with time-independent bulk modulus because that is a good approximation for most isotropic, viscoelastic materials. These transversely-isotropic materials, however, do not place any restrictions on which properties are time dependent. As result, it can model an isotropic material with a time-dependent bulk modulus as a special case. Imagine an isotropic material with K(t) and G(t) as time-dependent bulk and shear moduli, respectively. To model using a transversely isotropic material, choose GA(t) = GT(t) = G(t) along with:

      [math]\displaystyle{ K_T(t) = K(t) + \frac{G_T(t)}{3},\quad n(t)= K(t) + \frac{4G_T(t)}{3},\quad {\rm and}\quad \ell(t) = K(t) - \frac{2G_T(t)}{3} }[/math]

Finally, any other material properties (such as thermal expansion coefficients) should be set to the special cases for an isotropic material.

Effective Time Implementation

This material handles effect of temperature and solvent concentration on relaxation times by the same methods used for isotropic viscoelastic materials.

Elastic Mechanical Properties

This material handles effect of temperature and solvent concentration on elastic properties by the same methods used for isotropic viscoelastic materials.

Material Properties

The unusual task for this material is to use multiple terms to define the exponential series used for up to five material properties.

Property Description Units Default
GT0 The long term (or fully-relaxed) transverse shear modulus pressure units none
GA0 The long term (or fully-relaxed) axial shear modulus pressure units none
KT0 The long term (or fully-relaxed) plane-strain bulk modulus pressure units none
en0 The long term (or fully-relaxed) C33 element of the stiffness tensor pressure units none
ell0 The long term (or fully-relaxed) C13=C23 elements of the stiffness tensor pressure units none
ntaus The number of relaxation times of the previous long-term property that was entered. This property is only needed in XML files and must come before any subsequent Pk or tauk properties. In scripted files, the number is automatically determined from the number of relaxation times you provide. none none
Pk The next property in the series for the previous long-term property that was entered. Use multiple Pk values for each term on the series. pressure units none
tauk The next relaxation time in the series for the previous long-term property that was entered. Enter multiple tauk values for each term on the series. time units none
Tref Reference temperature to shift relaxation times using the WLF equation. If Tref<0, then no shifting is done and relaxation times will be independent of temperature. K -1
C1 Coefficient in WLF equation used when Tref≥0 to shift relaxation times. If the entered value is negative, the thermal shift switches to Arrhenious activation energy with ΔHa = -RC1, none 17.44
C2 Coefficient in WLF equation used when Tref≥0 to shift relaxation times (not used if C1 is negative). none 51.6
mref Reference concentration to shift relaxation times using the WLF-style equation. If mref<0, then no shifting is done and relaxation times will be independent of concentration. K -1
Cm1 Coefficient in WLF-style equation used when mref≥0 to shift relaxation times none 10
Cm2 Coefficient in WLF-style equation used when mref≥0 to shift relaxation times (must be positive) none 0.0625
bTemp
bTValue
Enter (bTemp,bTValue) pairs for piecewise interpolation of vertical temperature shift of elastic properties. Enter any number of pairs with bTemp values monotonically increasing (degrees,none) none
bConc
bCValue
Enter (bConc,bCValue) pairs for piecewise interpolation of vertical concentration (or moisture) shift of elastic properties. Enter any number of pairs with bConc values monotonically increasing. Enter with actual concentration and not concentration potential. none none
TI Properties Enter thermal expansion, solvent expansion, and poroelasticity properties as usual for transversely isotropic materials. varies varies
swapz Set to >0 to move axial direction from z axis to the y axis (or from θ axis to Z axis in axisymmetric calculations). This property is only needed for 2D simulations that want axial direction in the analysis plane (it is not allowed in 3D MPM simulations). none 0
(other) Properties common to all materials varies varies

The material properties need to define the time dependence 5 properties. The process for each one is to enter the long-term value first (GT0, GA0, KT0, en0, ell0) and then to follow each one by ntaus (only needed in XML files) and by one Pk and tauk value for each term in the series. Elastic value, or the property values at time zero, are sums of all Pk terms for that property. For example:

      [math]\displaystyle{ G_T(0) = G_{T0} + \sum_{k=1}^{N_{GT}} G_{Tk} }[/math]

Other elastic properties are given by

      [math]\displaystyle{ \nu_A(0) = {\ell(0)\over 2K_T(0)} \qquad {\rm and} \qquad E_A(0) = n(0) - 4K_T(0)\nu_A^2 = n(0) - \frac{\ell(0)^2}{K_T(0)} }[/math]

      [math]\displaystyle{ \frac{1}{E_T(0)} = \frac{1}{4K_T(0)} +\frac{1}{4G_T(0)} + {\nu_A(0)^2\over E_A(0)} \qquad {\rm and} \qquad \nu_T(0) = \frac{E_T(0)}{2G_T(0)}-1 }[/math]

For valid modeling, the initial Poisson's ratios must satisfy

      [math]\displaystyle{ -1\lt \nu_T(0)\lt 1 \qquad -\sqrt{E_A(0)\over E_T(0)} \lt \nu_A(0) \lt \sqrt{E_A(0)\over E_T(0)} \qquad {E_T(0)\nu_A(0)^2\over E_A(0)} \lt {1-\nu_T(0)\over 2} }[/math]

These relations must apply for all time, but only the initial values are validated before starting a simulation.

Deprecated Material Properties

Prior to the swapz material property, there were two types on transversely isotropic viscoelastic materials named "TIViscoelastic 1" and "TIViscoelastic 2". Although these can still be used as the material type, they are deprecated. The prior "TIViscoelastic 1" is identical to this material with swapz=0. The prior "TIViscoelastic 2" material is identical to this material with swapz=1.

History Variables

This material tracks internal history variables (one for each relaxation time and each component of stress) for implementation of linear viscoelastic properties, but currently none of these internal variables are available for archiving.

Example